|Place of Origin:||China|
|Model Number:||Beaded Equal 90 Degree Tees|
|Minimum Order Quantity:||100piece|
|Payment Terms:||Western Union, L/C, T/T, D/P, D/A, MoneyGram|
|Standard:||3x3/4 Inch Beaded Equal 90 Degree Tees||Surface Treatment:||Hot Dipped Galvanized And Cold Galvanized|
black iron tee fitting,
reducing tee pipe fitting
How about the leyon malleable cast iron's quality ?
We have 26 steps of process during producing the products ,over 6 steps of checking .
Firstly : Checking the scrap steel , the wP content should not be very high , the wP in malleable
cast iron should be lower than 0.1% . If it is very high , the malleable cast iron will break easily .
Secondly: Examing roughcast
Thirdly: Checked the cooked rough
Fourth: Destructive testing
Fifth: hot galvanized testing
Sixth: check the products
We do this just to make sure the quality of the products are good .
|Standard||Thread: ISO 7/1|
|Dimension||ISO 49, DIN 2950,EN10242|
|Chemical property||(C %2.4-2.9), (Si %1.4-1.9), (Mn %0.4-0.65), (P% <0.1), (S% <0.2%)|
|Physical property||Tensile strength>=350Mpa,Elongation>=10% Hardness<=150HB|
|Type||Beaded with ribs or banded with ribs|
|Beaded without ribs or banded without ribs|
|Surface||Galvanized/ no galvanized|
|Model||Elbow, Tees, Crosses, Bends, Unions, Bushings, Lateral Braches, Sockets, Nipples, Hexagon/Round, Caps, Plugs, Locknuts, Flanges ,Side Outlet Tees, Side Outlet Elbows and etc|
|Application||Suitable for pipe connect of steam, air, gas, oil and so on|
|Buyer’s drawings or designs are available|
|Package||Cartons without pallet|
|Cartons with pallet|
|Double woven bags|
|Or as buyer’s requirements|
||According to the quantities and specifications of each order|
|Normal delivery time is from 30 to 45 days after receiving the deposit
What’s malleable cast iron ?
Malleable cast iron is produced from white cast iron, which is made from hot liquid iron with certain chemical components. The white cast iron needs to be treated by malleablizing, such as graphitizing or oxidation and decarbonization, then its metallographic structures or chemical components will be changed, so can become into malleable cast iron.